Synthesis, Characterization and Catalytic Activity of Supported NiMo Catalysts



Guevara Lara, Alfredo

2011

K. Martínez-Juárez R. Silva-Rodrigo, A. Castillo-Mares, A. Guevara-Lara, J. A. Melo-Banda, A. Vázquez-Rodríguez, E. Terres-Rojas, "Synthesis, Characterization and Catalytic Activity of Supported NiMo Catalysts" Topics in Catalysis, Vol. 54, No. 8-9, (2011) 535-546, ISSN: 1022-5528 (Print) 1572-9028 (Online). DOI 10.1007/s11244-011-9618-9. Link: http://www.springerlink.com/content/k00n632m258k6688. Factor de impacto (2009): 2.379.


Abstract


A study of NiMo catalysts supported on MCM41 modified with alumina prepared by the solgel method is presented. NiMo phases were impregnated on the supports using the solution method with the purpose to obtain a material whose hexagonal structure of the MCM41 would not be affected with the addition of these active phases. The impregnation of the metals method used in the present work was outstanding, the textural properties of the catalysts decreased from 42 to 67%. There was a diminution in the textural properties of the catalysts with respect to the supports, nevertheless the prepared materials had more significant textural properties that the conventional catalysts of HDS. The adsorptiondesorption isotherms of the catalysts did not change considerably with the support source. By DRX was determined the structural properties of the metallic phases present in the material where phases such as NiMoO4, MoO3 and NiO were observed. Support wall thickness was increased with the incorporation of Ni and Mo metals into the materials. By means of Raman spectroscopy, the presence of MoO3 and Mo8O26 4? species was corroborated. Through UVvis where determined NiO of octahedral symmetry as well as Mo of tetrahedral and octahedral symmetry. The main reaction products were biphenyl (BP), cyclohexylbenzene (CHB) and bicyclohexyl (BCH) when the materials were tested in the HDS of DBT.



Producto de Investigación




Artículos relacionados

Cobalt Electrodeposition Process from Electrolytic Baths based on CoSO4 and (NH4)2SO4. Influence of ...

Morphological and magnetic properties of cobalt nanoclusters electrodeposited onto HOPG

Zinc Electrodeposition from Chloride Solutions onto Glassy Carbon Electrode

A theoretical quantum study on the distribution of electrophilic and nucleophilic active sites on th...

Nucleation and Growth Kinetics of Electrodeposited Sulfate-Doped Polypyrrole: Determination of the D...

Electrochemical kinetic study about cobalt electrodeposition onto GCE and HOPG substrates from sulfa...

A theoretical quantum study on the distribution of electrophilic and nucleophilic active sites on Ag...

A Semiempirical PM6 Study of Some Aminopyrimidine Derivatives and their Interaction with an Iron Sur...

Potentiometric behavior of graphite-epoxy electrochemical transducers towards anions, cations and pH...

Cobalt electrodeposition on polycrystalline palladium. Influence of temperature on kinetic parameter...